Alloy Navigator

Find the grade your specification needs.

965 references, 230 alloys, group-wide. Filter by industry, property, form or standard.

HardiallTS 160U

Bars

19 ≤ Ø < 40 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 1,069 MPa
Hardness: 34 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTS 160U

Bars

Bars - Wrought, solution heat treated, cold worked and spinodal heat treated, 19 ≤ Ø < 40 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 1,069 MPa
Hardness: 34 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTS 160U

Bars

40 ≤ Ø < 82 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 1,035 MPa
Hardness: 34 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTS 160U

Bars

Bars - Wrought, solution heat treated, cold worked and spinodal heat treated, 40 ≤ Ø < 82 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 1,035 MPa
Hardness: 34 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

15 ≤ Ø ≤ 108 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

Bars - Wrought, solution heat treated and spinodal heat treated, 15 ≤ Ø ≤ 108 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

Hollow bars - Wrought, solution heat treated and spinodal heat treated (length limited to 1000 mm / 39.37 in.), 50 ≤ OD < 217.4 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

Hollow bars, 50 ≤ OD < 217.4 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

Hollow bars, 50 ≤ OD < 217.4 mm, Thickness: 10 to 20 % of OD

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Tubes

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 277 HB
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

108 < Ø ≤ 170 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

HardiallTX 110

Bars

Bars - Wrought, solution heat treated and spinodal heat treated, 108 < Ø ≤ 170 mm

CuNiSn

CuNi15Sn8 · C72900

Copper-Nickel-Tin

Yield strength: 760 MPa
Hardness: 30 HRC
Density: 8.94 g/cm³
El. conductivity: 4.4 MS/m

View product

ZA9F / H3

Bars

Hollow bars, Section ≤ 2 000 mm²

CuZnAlMn

CuZn19Al6MnFe

Brasses

Yield strength: 590 MPa
Hardness: 225 HB
Density: 7.6 g/cm³
El. conductivity: 3 MS/m

View product

ZA9F / H3

Bars

Section ≤ 2 000 mm²

CuZnAlMn

CuZn19Al6MnFe

Brasses

Yield strength: 590 MPa
Hardness: 225 HB
Density: 7.6 g/cm³
El. conductivity: 3 MS/m

View product

K5

Bars

127 ≤ Section ≤ 2 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 590 MPa
Hardness: 215 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

K5Extruded or forged

Bars

127 ≤ Section ≤ 2 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 590 MPa
Hardness: 215 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

K7

Bars

12.7 < Ø ≤ 50 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 640 MPa
Hardness: 230 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

K7

Bars

50 < Ø ≤ 127 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 590 MPa
Hardness: 225 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

K7Extruded

Bars

12.7 < Ø ≤ 50 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 640 MPa
Hardness: 230 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

K7Extruded or forged

Bars

50 < Ø ≤ 127 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 590 MPa
Hardness: 225 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

K7

Bars

127 < Ø ≤ 250 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 550 MPa
Hardness: 225 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

K7Extruded or forged

Bars

127 < Ø ≤ 250 mm

CuNiAlFe

CuNi14Al3Fe1

Copper-Nickel

Yield strength: 550 MPa
Hardness: 225 HB
Density: 8.5 g/cm³
El. conductivity: 6 MS/m

View product

NC4 AMS 4640HR50

Bars

25.4 < Ø ≤ 50.8 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 413 MPa
Hardness: 201 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640HR50

Bars

9.5 ≤ Ø ≤ 25.4 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 469 MPa
Hardness: 201 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

K5

Bars

2 000 < Section ≤ 11 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 540 MPa
Hardness: 205 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

K5Extruded or forged

Bars

2 000 < Section ≤ 11 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 540 MPa
Hardness: 205 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

NCS AMS 4590M

Bars

13 ≤ Ø ≤ 200 mm

CuAlNiFe

CuAl11Ni5Fe5 · C63020

Copper-Aluminium

Yield strength: 390 MPa
Hardness: 185 HB
Density: 7.5 g/cm³
El. conductivity: 5 MS/m

View product

NCS AMS 4590M

Bars

Hollow bars, 50 < OD ≤ 250 mm

CuAlNiFe

CuAl11Ni5Fe5 · C63020

Copper-Aluminium

Yield strength: 390 MPa
Hardness: 185 HB
Density: 7.5 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640HR50

Bars

50.8 < Ø ≤ 76.2 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 379 MPa
Hardness: 187 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

K5

Bars

11 000 < Section ≤ 49 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 500 MPa
Hardness: 200 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

K5Extruded or forged

Bars

11 000 < Section ≤ 49 000 mm²

CuNiAl

CuNi14Al2, CuNi14Al3

Copper-Nickel

Yield strength: 500 MPa
Hardness: 200 HB
Density: 8.9 g/cm³
El. conductivity: 5 MS/m

View product

CA104

Bars

16 ≤ Ø ≤ 18 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 400 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104

Bars

18 < Ø ≤ 80 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 370 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104

Bars

Hollow bars, 50 ≤ OD ≤ 80, Thickness ≥ 10 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 370 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104Extruded

Bars

16 ≤ Ø ≤ 18 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 400 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104Extruded

Bars

18 < Ø ≤ 80 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 370 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104Extruded

Bars

Hollow bars, 50 ≤ OD ≤ 80, Thickness ≥ 10 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 370 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640M

Bars

9.5 ≤ Ø ≤ 280 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 180 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640M

Bars

Hollow bars, 50 ≤ OD ≤ 280 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 180 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640HR50, TQ50

Bars

76.2 < Ø ≤ 254 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 345 MPa
Hardness: 187 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC4 AMS 4640HR50, TQ50

Bars

Hollow bars, OD ≥ 50 mm, Thickness ≥ 10 mm

CuAlNiFe

CuAl10Ni5Fe4 · C63000

Copper-Aluminium

Yield strength: 345 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2

Bars

15 ≤ Ø ≤ 25 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 325 MPa
Hardness: 165 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2Extruded

Bars

15 ≤ Ø ≤ 25 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 325 MPa
Hardness: 165 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104

Bars

Hollow bars, OD > 80 mm, Thickness ≥ 10 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104

Bars

Ø > 80 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104Extruded or forged

Bars

Hollow bars, OD > 80 mm, Thickness ≥ 10 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

CA104Extruded or forged

Bars

Ø > 80 mm

CuAlNiFe

CuAl10Ni5Fe4

Copper-Aluminium

Yield strength: 320 MPa
Hardness: 190 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2

Bars

25 < Ø ≤ 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 295 MPa
Hardness: 160 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2Extruded or forged

Bars

25 < Ø ≤ 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 295 MPa
Hardness: 160 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2

Bars

Hollow bars, OD > 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 250 MPa
Hardness: 150 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2

Bars

Ø > 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 250 MPa
Hardness: 150 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2Extruded or forged

Bars

Hollow bars, OD > 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 250 MPa
Hardness: 150 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

NC2Extruded or forged

Bars

Ø > 100 mm

CuAlNiFe

CuAl9Ni5Fe4

Copper-Aluminium

Yield strength: 250 MPa
Hardness: 150 HB
Density: 7.6 g/cm³
El. conductivity: 5 MS/m

View product

Si45ZCold worked

Bars

15.88 ≤ Ø ≤ 76.2 mm

CuSiFeZn

CuSi3Fe2Zn3 · C65620

Brasses

Yield strength: 340 MPa
Hardness: 150 HB
Density: 8.6 g/cm³
El. conductivity: 5 MS/m

View product

Si45ZAs-manufactured or Stress relieved

Bars

15.88 ≤ Ø ≤ 152.4 mm

CuSiFeZn

CuSi3Fe2Zn3 · C65620

Brasses

Yield strength: 140 MPa
Hardness: 90 HB
Density: 8.6 g/cm³
El. conductivity: 5 MS/m

View product

Si45ZAs-manufactured or Stress relieved

Bars

Hollow bars, 63.5 ≤ OD ≤ 231.78 mm, ID ≥ 35 mm, Thickness ≥ 10 mm

CuSiFeZn

CuSi3Fe2Zn3 · C65620

Brasses

Yield strength: 140 MPa
Hardness: 90 HB
Density: 8.6 g/cm³
El. conductivity: 5 MS/m

View product

Standards — Grades are listed under EN, ASTM/UNS and DIN designations.